Homopolymer Polypropylene Plastic Resin Raw Material Pph T03 Yarn Injection Grade

• Customization: Available
• Feature: Biodegradable
• CAS No.: 9003-07-0
• Model NO.: T03
• Material: Polypropylene/PP
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Type: 100% Virgin Material
• Other Name: PP Granule /Polypropylene Resin/ PP Resin
• Melt Flow Rate: 3.3G/10 Min
• Transport Package: Bag
• Specification: 25 Kgs
• Trademark: Grand
• Origin: China
• HS Code: 3902100090
• Production Capacity: 5000 Tons Per Month

Product Description

Product Description

 Polypropylene, referred to as PP, is a polymer made of propylene by addition polymerization. It is a white waxy material with a transparent and light appearance. The chemical formula is (C3H6)n, the density is 0.89 ~ 0.91g/cm3, flammable, the melting point is 164~170ºC, it is softened at about 155ºC, and the use temperature range is -30 ~ 140ºC. It can resist the corrosion of acid, alkali, salt solution and a variety of organic solvents below 80ºC, and can decompose under high temperature and oxidation. Polypropylene is a thermoplastic synthetic resin with excellent properties.
    It is a colorless semi-transparent thermoplastic lightweight general purpose plastic with chemical resistance, heat resistance, electrical insulation, high strength mechanical properties and good high wear resistance. It is widely used
in the production of clothing, blankets and other fiber products, medical equipment, automobiles, bicycles, parts, transportation pipes, chemical containers, etc., and is also used in food and medicine packaging.

Product Parameters

Film Grade

Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C

Blown Grade

Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%

Injection grade

Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

Main Applications

1.Fiber ( Carpet, Textils, Upholstery, etc.)
2.Film ( shopping bags, casting film, multilayer film, etc.)
3.Blow Molding ( Medical & Cosmetic container, Lubricant & Paint container, etc)
4.Extrusion Molding ( Sheet, Pipe, Wire & Cable, etc.)
5.Injection Molding ( Automotive, Electronic, Construction, House wares, Furniture,Toys, etc.)

Packaging & Shipping

1.Packing:

25kg/bag, or per your requirement.18mt-20mt /20'FCL
2.Storage:
The resin should be stored in a drafty, dry warehouse and away from fire and direct sunlight. It should not be piled up in the open air.
3.Transportation:
During transportation, the product should not be exposed to strong sunlight or rain and should not be transported together with sand, soil, scrap metal, coal or glass. Transportation together with toxic, corrosive and flammable substance is strictly prohibited.

 

During transportation, the product should not be exposed to strong sunlight or rain and should not be transported together with sand, soil, scrap metal, coal or glass. Transportation together with toxic, corrosive and flammable substance is strictly prohibited.